Metallurgical Solutions, Inc


Salt Bath Heat Treatment (1000 TO 2300 F) of high speed, tool steels, carbon/low alloy steels and gray/ductile iron casting using salt, air or oil quenching.
Air Tempering Steam Tempering Salt Tempering Stress Relieving Annealing Solution Annealing Precipitation Hardening Martempering Austempering of Steel & Ductile Iron (ADI) Cryogenic Deep Freeze Crack Detection Hardness Testing Straightening Induction Heating Vacuum Furnace Processing Consulting Engineering/Failure Analysis Non-Destructive Testing Carburizing/Direct Quench Salt Bath Ferritic Nitrocarburizing (FNC)
Fluidized bed and salt marquench combination (Both 48 " working depth) for heat treating and quenching alloy and tool steels with minimum distortion. The fluidized bed furnace is used to austenitize, normalize, anneal, age harden, solution anneal, stress relieve and steam black oxide. View our Consulting Engineering Fee List

Programmable vacuum furnace heat-treating with nitrogen cool, for hardening, annealing, solution treating and Precipitation age hardening.

Induction heating, hardening both ends of machine gun ammunition belt tension lever.

Overbend straightening of machine spindle using 20 ton
Hydraulic press.

Peen straightening of hardened S7 tool steel pneumatic tool driver, to improve straightness.

Cryogenic treating of heat-treated tools and components to as low as -320 F.

Salt bath hardening of M42 HSS cutters, showing preheating, high temperature austenitizing and quenching steps in the cycle.

Fluidized bed annealing using nitrogen atmosphere, of 1095 steel investment castings.

Selective hardening of knife blades in salt bath, heat treating the blade only.

Carburize case hardening to 0.080 - 0.100" depth, AISI 9310 steel hydraulic Pistons, followed by salt bath marquenching to minimize distortion.